Surgical implant, method for the production and use thereof

ABSTRACT

A surgical implant is made from biocompatible fiber material as a woven textile fabric, in particular in the form of a vascular prosthesis, the woven fabric being so configured that its permeability to blood is so low that the blood impregnates the textile fabric upon implantation and seals it off by coagulating, but does not flow through it.

FIELD OF THE INVENTION

The invention relates to a surgical implant, a method for its productionand its use.

BACKGROUND

In the medical treatment of humans or animals it is often necessary, insurgical interventions, to support diseased or damaged body parts bymeans of implants or to replace these body parts partially, or evencompletely, by means of prostheses. Examples of such implants arevascular prostheses intended to replace damaged parts of blood vessels.Implants are known which have a knitted or woven structure. Moreover,vascular prostheses are known with structured surfaces, for examplepleats or velour.

In the known implants, there are problems regarding the process ofincorporation because the foreign body constituted by the implant iscolonized only slowly by endogenous cells. There are also difficultiesinvolved in sewing the prosthesis in place and connecting it to thepatient's body tissue. The porosity of known textile implants can causeleaking, with undesired blood loss. This can lead to increasedintraoperative complications, longer interruption of the blood supply tothe distal tissues and organs, or bleeding through the vessel walls,with risks of further postoperative complications, impairedincorporation of the implant, or, as a result of this, secondarydiseases.

The object is therefore to make available a surgical implant whichovercomes the problems of implants from the prior art, becomesincorporated rapidly and without complications in the patient's body,can be produced easily and inexpensively by conventional methods, and iseasy to apply in surgical practice.

This object is achieved by means of a surgical implant made frombiocompatible fiber material as a woven textile fabric, in particular inthe form of a vascular prosthesis, characterized in that the wovenfabric is so configured that its permeability to blood, to whichanticoagulants have been added, is so low that the blood impregnates thetextile fabric upon implantation and seals it off by coagulating.

Surprisingly, it was found that an implant according to the presentinvention becomes incorporated particularly rapidly and withoutcomplications. There is no accumulation of blood clots which canpermanently interfere with the creation of the neointima or the vesselcapsule.

Materials which can be used to form such an implant are biocompatiblenatural fibers, synthetic fibers, mixed fibers, composite fibers, ormixtures of these. One example of a preferred implant material ispolyethylene terephthalate (e.g. available commercially under the brandname Dacron).

The implant according to the invention can have a water permeability inthe range of from 100 to 300 ml/cm².min, in particular of from 150 to250 ml/cm².min. These water permeability values were measured at 120mmHg using the Wesolowski method of determination. In this way theimplant is found to be blood-tight after a short time, and the risk ofseeping hemorrhage is low.

The implant can advantageously be made so thin that it is possible forblood vessels to grow in. It can also be made so thin that it ispossible for nutrients to pass through in order to supply a neointima inthe process of formation. Intracellular and capillary diffusion oftissue fluid is possible. During the formation of a neointima, suchdiffusion from outside is advantageous for nutrient supply. This supplyis later provided by means of new vessel infiltrations.

In one embodiment of the invention, the woven fabric can be configuredin a thickness of from 0.1 to 0.35 mm, in particular of from 0.15 to0.25 mm, preferably 0.2 mm. Thickness is determined according to DIN863.

In a particular embodiment, the woven fabric of the implant can beconfigured with threads lying flat alongside one another without closecontact. The woven fabric can be preferably configured with threads ofyarn size 10 to 200 dtex, 10 to 200 filaments per thread, and a twistingof the yarn of 50 to 500 turns/m. In addition, the woven fabric can beconfigured with 30 to 120 warp threads and 10 to 70 weft threads percentimeter, in particular 40 to 80 warp threads and 20 to 50 weftthreads. According to the invention, the woven fabric can preferably beconfigured with a repeat of 8×8.

In the woven fabric of the implant, the spacing of the threads withrespect to one another can correspond to the thread width, so that thethreads lie close alongside one another. The small spacing betweenindividual fibers is important for irritation-free and rapidincorporation of the implant. If very large cells are able to collectbetween implant fibers, the ingrowth of the desired neointima isobstructed. The individual fibers of the thread can also lie flatalongside one another in the woven fabric, so that the thread crosssection is not round but instead oval. Typically, about 20 individualfibers can lie alongside one another in a flat thread in the wovenfabric. Flat fiber bundles with substantially parallel fibers can lie inparticular on the surface of the implant fabric.

In a preferred embodiment, the woven fabric of the implant can beconfigured essentially in a plain weave, in particular having a basestructure with a plain weave.

In a particular embodiment, it is possible for only flat threads to beused as warp threads. In one possible embodiment, it is possible foronly textured threads to be used as warp threads. Advantageously, thewoven fabric can be made up of a combination of flat and texturedthreads. The overall ratio of flat threads to textured threads canpreferably be between 1:1 and 6:1, in particular 3:1. In a particularembodiment, the woven fabric can according to the invention contain atleast 50% flat threads, that is to say nontextured threads.

In a preferred embodiment, flat and textured threads, particularly inalternating sequence, can be used as warp threads, the ratio of flatthreads to textured threads being between 2:1 and 1:2, in particular1:1.

In a particularly preferred embodiment of the implant according to theinvention, it is possible for only flat threads to be used as weftthreads. In another embodiment, flat and textured threads, particularlyin alternating sequence, can be used as weft threads, the ratio of flatthreads to textured threads being between 5:1 and 1:5. The implant mayadvantageously be characterized by flat threads being lightly plied.

In an advantageous embodiment of the implant according to the invention,floating threads can be included, in particular floating threadsextending in the warp direction. Such a floating thread is preferablypresent additionally to and parallel to a warp thread in the plainweave. At the site where it lies in plain weave, the additional floatingthread runs preferably together with the parallel warp thread and joinsup again with the warp thread after the floating. The floating threadscan preferably lie flat in the woven fabric surface and do not formloops. It is particularly advantageous for the floating threads to betextured.

In a preferred embodiment of the invention, a floating textured threadin the weave can lie in proximity to two flat threads running in thesame direction of the woven fabric. A float in the warp direction mayhave a favorable effect on the incorporation behavior in the case of atubular implant.

In a particular embodiment, a woven fabric can be made up only of flatthreads with a float of textured threads. In another embodiment, a wovenfabric can be made up of alternating flat and textured threads with afloat of textured threads, in which case in particular only every secondtextured thread has a float.

It is particularly advantageous that the floating threads can preferablyextend only in the warp direction. In another embodiment, the floatingthreads can extend both in the warp direction and in the weft direction,and in particular the floating threads can be included in the warpdirection and in the weft direction in different numbers.

According to the invention, the float can preferably extend over morethan 2 threads, in particular over 3 to 10 threads, preferably over 4 to6 threads. The float can advantageously be 4 to 6 over 1, preferably 5over 1. In a preferred embodiment of the invention, with a repeat of8×8, a float over 5 under 1 over 1 under 1 can be included. In thefloat, an uneven number is preferred, since otherwise the floatingthread no longer lies parallel to an adjacent woven fabric thread of theplain weave.

According to the invention, the ratio of floating threads to warpthreads can be between 1:20 to 1:1, in particular between 1:10 to 1:2,preferably 1:3. In other words, floating threads can be present in aproportion of about 5 to 50%, in particular of 9 to 33%, preferably 25%,in relation to warp threads in the woven fabric. The floats of adjacentfloating threads can preferably be offset in the warp direction, withpreferably at least some of the floats overlapping.

Advantageously, the mutual spacing between floating threads in the weftdirection can in each case be identical. In particular, at least threethreads of the basic woven fabric can lie between these. A maximum oftwo overlaps of warp threads can lie alongside one another in the weftdirection.

The implant according to the invention can be characterized in that thefloating threads float only on one surface of the implant, which ispreferably the outer surface in the case of a vascular prosthesis. In arefinement of this, a float can have only a slight pile height, inparticular only one occasioned by the texturing of the threads.

The woven fabric can advantageously be shrunk by thermal treatment. Inparticular, textured threads in the woven fabric can be opened by theshrinkage. In addition, the pile height of the woven fabric of theimplant can be influenced by shrinkage.

According to the invention, the implant, particularly on at least oneside of the woven fabric, can have a structure favoring ingrowth of aneointima. This is preferably a substantially pure plain weave withmainly flat threads and a small proportion of open textured threads.Mesothelial cells are able, starting from vessel stumps, to form a newthin and smooth neointima.

In a refinement of this, the implant can have, at least on one side,preferably the other side of the woven fabric, a structure favoring theformation of a thin fibrous capsule. Compared to the other side, thisside has the floats consisting in particular of textured threads.Fibroblasts grow in from surrounding tissue and form the collagen forexternal encapsulation free from blood clots.

According to the invention, the woven fabric can be configured as asimple velour. Advantageously, a velour structure of the implant may beprovided only on the vessel's outside. Moreover, the inner side of thevessel can have a structure favoring ingrowth of a neointima. Such alayer of mesothelial cells can form in particular on a smooth wall ofthe woven fabric structure. Preferably, the implant according to theinvention can have on one side, in particular on the side lying to theinside in the case of a vascular prosthesis, textured surface threads atless than 30%, in particular at less than 20% of the intersections ofwarp and weft. By parallel arrangement of textured additional floatingthreads with flat threads of the basic woven fabric running in the samedirection, the proportion of textured threads is further reduced bypartial overlapping of the textured thread by the flat thread. Moreover,preferably on the outward side in the case of a vascular prosthesis, theimplant according to the invention can, at fewer than half and inparticular at fewer than a third of the intersections of warp and weft,have textured threads lying on the surface. In this way, on one side ofthe implant fabric with preferably only a plain weave, the floatingthread can be at least partially covered by normal, flat, parallelthreads of the basic fabric of the plain weave, and, on the other side,can extend on a normal thread of the basic fabric of the plain weave andlie substantially exposed on the fabric surface.

By the preferable use of the plain weave on the inner side of a vascularprosthesis, a smooth inner surface is produced. On the outside, bycontrast, the textile structure according to the invention, with moreuse of textured yarns, produces a voluminous structure compared to theinner side. By means of this more strongly structured outer surface, adensity gradient (porosity gradient) is obtained toward the innersurface of the vascular prosthesis, resulting in improved ingrowth ofthe blood vessels and, at the same time, more favorable formation of theneointima.

If desired in special cases, a rapidly absorbable coating, for exampleof gelatin or other suitable natural or synthetic materials, can beapplied to the implant according to the invention. However, this is notgenerally necessary, because the woven fabric seals upon the firstpassage of blood.

The invention also relates to a method for the production of a surgicalimplant from biocompatible fiber material as a woven textile fabric, inparticular in the form of a vascular prosthesis, said method beingcharacterized in that, by means of weaving, a structure is formed whosepermeability to blood, to which anticoagulants have been added, is solow that the blood impregnates the textile fabric and seals it off bycoagulating.

From a textile fabric produced according to the invention, in [sic]implant of desired shape can be produced by textile techniques known tothose skilled in the art. For use as a vascular prosthesis, the implantcan be configured in the shape of a tube with a suitable lumen.

Moreover, one or more medically active substances can advantageously beadded to the implant according to the invention. These active substancesmay be, for example, medicaments, antibiotics, antiseptics, clottingfactors, growth factors and the like.

The implant produced according to the invention can be made ready formedical use in a manner known per se. In particular, the materialaccording to the invention can be suitably sterilized. An appropriatesterilization method can be chosen from the usual physical or chemicalmethods for inactivation of microorganisms or can be a combination ofsuch methods. One possible sterilization method involves treatment withgamma radiation. Another method of sterilizing the implant materialaccording to the invention for medical purposes involves using ethyleneoxide. The medical implant produced can advantageously be cut to theappropriate size and suitably packed ready for use.

The invention further relates to the use of a surgical implant, inparticular in the form of a vascular prosthesis for treating bloodvessel defects in human medicine and veterinary medicine.

When the vascular prosthesis produced according to the invention wastested on animals (dogs), it was found to be blood-tight. To implant thevascular prosthesis according to the invention as an infrarenal aortareplacement, the affected portion of the aorta is exposed, the proximaland distal ends of the vessel are clamped, and the anticoagulant heparinis injected. After resection of the exposed portion, the proximalanastomosis is established. The distal end of the prosthesis is thenlikewise closed with a clamp, and the proximal clamp is briefly openedso that heparinized blood passes into the implant and displaces the aircontained therein. The proximal clamp is then closed for 15 seconds, andthe blood emerging through the implant is swabbed up. Renewed opening ofthe clamped proximal end of the prosthetic implant causes a secondpressure surge of blood, already with considerably less blood flowingthrough the prosthesis. The blood penetrating into the woven fabric ofthe implant coagulates in the vessel wall and thus leads to sealing ofthe vascular prosthesis. Blood has to run through about two to threetimes before the vascular prosthesis is sealed off. The distal end ofthe implant is then also closed by suturing.

After implantation, a thin layer of fibrin quickly forms in the wall ofthe vascular prosthesis. This is physiologically broken down withoutproblem, while a neointima and an outer layer of collagen are built up.Surprisingly, after just three months, there has been uniform formationof a bright neointima. Three months after implantation there is also athin transparent fibrous capsule. After six months, the implant hasbecome incorporated without complications and without inflammation.

In the implant according to the invention, it is not just the porositythat is important, but also the size of the pores and the pore sizedistribution, produced by the different density of the threadarrangement with different air content in the woven wall. Only minimalbleeding occurs in the wall, and so there is little in the way of bloodclots, the presence of which may cause problems and which have to bebroken up.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram showing a weave pattern of a vascular prosthesisfabricated as a basic woven fabric in a plain weave, with floating inthe warp direction.

DETAILED DESCRIPTION

Further features and details of the invention will become clear from thefollowing description of a preferred embodiment which is given as anexample and with reference to the accompanying figure. The individualfeatures can be implemented singly, or can be implemented severally incombination with one another. The example serves only to illustrate thepresent invention, and the latter is in no way intended to be restrictedthereto.

EXAMPLE

A vascular prosthesis is made from biocompatible synthetic fibermaterial (polyethylene terephthalate) by weaving of a basic woven fabricin a plain weave, with floating in the warp direction. The weave patternis shown in FIG. 1.

The warp threads used are flat (100 filaments 80 dtex Z-twist 240 turns)and textured (100 filaments 80 dtex Z-twist 140 turns) threads, everythird warp thread of the fabric of the plain weave being textured. Theweft comprises only flat threads (100 filaments 80 dtex). The floatingthread is textured (50 filaments 40/2 dtex).

All warp and weft threads are arranged in a plain weave. The wovenfabric is configured with 31 weft threads and 68 warp threads percentimeter. In a repeat of 8×8, the floating thread is includedadditionally to the 1st and 5th warp thread. The floating is offset overthree warp threads. In the weft direction, the floating thread in eachcase floats over five weft threads, so that the float appears only onone side of the woven fabric.

In this way, four textured threads are present in the warp direction perrepeat, two of them in the basic fabric of the plain weave and two ofthem as additional floating threads. The additional textured floatingthreads each lie between two flat threads. Since the floating thread istextured, it forms a structure on one surface of the woven fabric. Onthe other side of the woven fabric, the floating thread lies alongsidethe warp thread in the plain weave and on this side does not contributeto a structuring.

The water permeability of this woven fabric lies in the range of 200+50ml/cm²/min, as measured at 120 mmHg by the Wesolowski method ofdetermination.

The wall thickness of the uncoated prosthesis is 0.15 to 0.25 mm. Thewall thickness is measured in accordance with DIN 863 by means of amicrometer gage whose measurement spindle is driven via a coupling. Theforce acting on the measurement surface is 5 to 10 N. The measurement isperformed on a vascular prosthesis cut open, with any creasing beingsmoothed out.

For vascular prostheses with an external diameter of from 6 mm to 38 mm,the wall thickness of the woven fabric is approximately the same, with adeviation of +0.01 mm.

1. A surgical implant made from biocompatible fiber material as a woventextile fabric, including warp and weft threads, in the form of avascular prosthesis, the woven textile fabric configured essentially ina plain weave and having a base structure in plain weave, the woventextile fabric configured to have a permeability to blood, to whichanticoagulants have been added, said blood permeability sufficiently lowthat the blood impregnates the textile fabric upon implantation andseals it off by coagulating, and the woven textile fabric having a waterpermeability in the range of 100 to 300 ml/cm² per minute, wherein thewoven fabric is configured with 30 to 120 warp threads and 10 to 70 weftthreads per centimeter, only flat threads are used as weft threads, andflat and texturized threads are used as warp threads, the ratio of flatthreads to textured threads in the warp threads being between 2:1 to 1:2and textured floating threads extending in the warp direction areincluded that float only on the outer surface of the vascular prosthesisand the floating threads lie flat in the woven textile fabric surfaceand do not form loops.
 2. The implant as claimed in claim 1, wherein thewoven textile fabric has a water permeability in the range of from 150to 250 mI/cm2 per mm.
 3. The implant as claimed in claim 1, comprisingthe woven textile fabric configured sufficiently thin that it ispossible for blood vessels to grow through.
 4. The implant as claimed inclaim 1, comprising the woven textile fabric configured sufficientlythin that it is possible for tissue fluid to pass through in order tosupply a neointima in the process of formation.
 5. The implant asclaimed in claim 1, wherein the woven textile fabric is configured in athickness of from 0.1 to 0.35 mm.
 6. The implant as claimed in claim 1,wherein the woven textile fabric is configured with threads of yarn size10 to 200 dtex, 10 to 200 filaments per thread, and a twisting of theyarn of 50 to 500 turns/m.
 7. The implant as claimed in claim 1, whereinthe floating extends over more than 2 threads.
 8. The implant as claimedin claim 1, comprising floating warp threads and warp threads lying in aplain weave having a ratio of floating warp threads to warp threadslying in the plain weave between 1:2 to 1:1.
 9. The implant as claimedin claim 1, wherein a float has only a small pile height.
 10. Theimplant as claimed in claim 1, wherein the implant has an inner surfaceand an outer surface, wherein the inner surface is substantially smooth,and the outer surface is preferably structured.
 11. A method fortreating blood vessel defects in human medicine and veterinary medicine,wherein the implant as claimed in claim 1 is used in surgery in the formof a vascular prosthesis.
 12. A method for the production of an implantfor use in surgery and made from biocompatible fiber material as a woventextile fabric, including warp and weft threads, in the form of avascular prosthesis, the woven textile fabric configured essentially ina plain weave and having a base structure in plain weave, wherein, bymeans of weaving, a structure is formed whose permeability to blood, towhich anticoagulants have been added, is so low that the bloodimpregnates the textile fabric and seals it off by coagulating, whereinthe woven fabric is configured with 30 to 120 warp threads and 10 to 70weft threads per centimeter, only flat threads are used as weft threads,and flat and texturized threads are used as warp threads, the ratio offlat threads to textured threads in the warp threads being between 2:1to 1:2 and textured floating threads extending in the warp direction areincluded that float only on the outer surface of the vascular prosthesisand the floating threads lie flat in the woven textile fabric surfaceand do not form loops.
 13. A method as claimed in claim 12, wherein theimplant is in the form of a vascular prosthesis.
 14. A surgical implantmade from biocompatible fiber material as a woven textile fabric,including warp and weft threads, in the form of a vascular prosthesis,the woven textile fabric configured essentially in a plain weave andhaving a base structure in plain weave, with flat threads used as weftthreads, flat and texturized threads used as warp threads, and a ratioof flat threads to textured threads selected to provide a goodinterconnection of the implant and connective tissue in the patient'sbody while retarding hemorrhage and undesirable formation of cicatricialtissue, the woven textile fabric configured to have a permeability toblood, to which anticoagulants have been added, said blood permeabilitysufficiently low that the blood impregnates the textile fabric uponimplantation and seals it off by coagulating, and the woven textilefabric having a water permeability in the range of 100 to 300 ml/cm² perminute, wherein the woven fabric is configured with 30 to 120 warpthreads and 10 to 70 weft threads per centimeter, only flat threads areused as weft threads, and flat and texturized threads are used as warpthreads, the ratio of flat threads to textured threads in the warpthreads being between 2:1 to 1:2 and textured floating threads extendingin the warp direction are included that float only on the outer surfaceof the vascular prosthesis and the floating threads lie flat in thewoven textile fabric surface and do not form loops.
 15. The implant asclaimed in claim 14, comprising the woven textile fabric configuredsufficiently thin that it is possible for blood vessels to grow throughin order to supply a neointima in the process of formation.